RTP 1805
丙烯酸 (PMMA)
RTP Company
Warning: The status of this material is 'Commercial: Limited Issue'
The data for this material has not been recently verified.
Please contact RTP Company for current information prior to specifying this grade.
-Preliminary Product Data per RTP Co.-
The value listed as UL 94, was tested in accordance with RTP Company test methods.
| 基本信息 | |
|---|
| 填料/增强材料 | |
| RoHS 合规性 | |
| 外观 | |
| 形式 | |
| 加工方法 | |
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 比重 | 1.42 | g/cm³ | ASTM D792 |
| 收缩率 -
流动 (3.18 mm) | 0.10 | % | ASTM D955 |
| 吸水率 (23°C, 24 hr) | 0.20 | % | ASTM D570 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|
| 洛氏硬度 (R 级) | 120 | | ASTM D785 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 拉伸模量 | 10300 | MPa | ASTM D638 |
| 抗张强度 | 103 | MPa | ASTM D638 |
| 伸长率 (断裂) | 1.0 | % | ASTM D638 |
| 弯曲模量 | 10300 | MPa | ASTM D790 |
| 弯曲强度 | 152 | MPa | ASTM D790 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 悬壁梁缺口冲击强度 (3.18 mm) | 53 | J/m | ASTM D256 |
| 无缺口悬臂梁冲击 (3.18 mm) | 160 | J/m | ASTM D4812 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 载荷下热变形温度 | | | ASTM D648 |
| 0.45 MPa, 未退火 | 98.9 | °C | ASTM D648 |
| 1.8 MPa, 未退火 | 93.3 | °C | ASTM D648 |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 体积电阻率 | 1.0E+17 | ohms·cm | ASTM D257 |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
|---|
| UL 阻燃等级 (1.59 mm) | HB | | UL 94 |
| 补充信息 |
|---|
| Mold Shrinkage, Linear-Flow, ASTM D-955, 0.25in.: 2mil/in. |
| 注射 | 额定值 | 单位制 | |
|---|
| 料筒后部温度 | 218 到 274 | °C | |
| 料筒中部温度 | 218 到 274 | °C | |
| 料筒前部温度 | 218 到 274 | °C | |
| 模具温度 | 23.9 到 65.6 | °C | |
| 注塑压力 | 68.9 到 103 | MPa | |
此数据由 承扬 从该材料的生产商处获得。承扬 尽最大努力确保此数据的准确性，但是承扬对这些数据值不承担任何责任，并强烈建议在最终选料前，就数据值与材料供应商进行验证。