| Thermal properties |
|---|
| 属性名称 | 测试标准 | 测试标准 | 单位 | 数值 |
|---|
| Burning behavior UL 94 [UL recognition] | UL 94 | 0.85 mm | Class | HB |
| Coefficient of linear thermal expansion, normal | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.75 |
| Coefficient of linear thermal expansion, parallel | ISO 11359-1,-2 | 23 to 55 °C | 10^-4^/K | 0.43 |
| Temperature of deflection under load | ISO 75-1,-2 | 0.45 MPa | °C | 130 |
| Temperature of deflection under load | ISO 75-1,-2 | 1.80 MPa | °C | 114 |
| Vicat softening temperature | ISO 306 | 50 N; 120 °C/h | °C | 130 |
| Vicat softening temperature | ISO 306 | 50 N; 50 °C/h | °C | 128 |
| Mechanical properties (23 °C/50 % r. h.) |
|---|
| 属性名称 | 测试标准 | 测试标准 | 单位 | 数值 |
|---|
| Izod impact strength | ISO 180/U | -30 °C | kJ/m² | 45 |
| Izod impact strength | ISO 180/U | 23 °C | kJ/m² | 60 |
| Izod notched impact strength | ISO 180/A | 23 °C | kJ/m² | 14 |
| Izod notched impact strength | ISO 180/A | -30 °C | kJ/m² | 6 |
| Strain at break | ISO 527-1,-2 | 5 mm/min | % | 10 |
| Stress at break | ISO 527-1,-2 | 5 mm/min | MPa | 42 |
| Tensile modulus | ISO 527-1,-2 | 1 mm/min | MPa | 4300 |
| Yield strain | ISO 527-1,-2 | 5 mm/min | % | 4.2 |
| Yield stress | ISO 527-1,-2 | 5 mm/min | MPa | 60 |
| Rheological properties |
|---|
| 属性名称 | 测试标准 | 测试标准 | 单位 | 数值 |
|---|
| Melt viscosity | b.o. ISO 11443-A | 1000 s^-1^/ 260 °C | Pa*s | 215 |
| Melt volume-flow rate | ISO 1133 | 260 °C/ 5 kg | cm³/10 min | 16 |
| Molding shrinkage, normal | ISO 294-4 | 60x60x2 mm/ 260 °C / MT 80 °C | % | 0.4 - 0.6 |
| Molding shrinkage, parallel | ISO 294-4 | 60x60x2 mm/ 260 °C / MT 80 °C | % | 0.4 - 0.6 |
| Electrical properties (23 °C/50 % r. h.) |
|---|
| 属性名称 | 测试标准 | 测试标准 | 单位 | 数值 |
|---|
| Comparative tracking index CTI | IEC 60112 | Solution A | Rating | 175 |
| Dissipation factor | IEC 60250 | 1 MHz | 10^-4^ | 127 |
| Dissipation factor | IEC 60250 | 100 Hz | 10^-4^ | 31 |
| Electrical strength | IEC 60243-1 | 1 mm | kV/mm | 36 |
| Relative permittivity | IEC 60250 | 1 MHz | | 3.2 |
| Relative permittivity | IEC 60250 | 100 Hz | | 3.3 |
| Surface resistivity | IEC 60093 | | Ohm | 1E16 |
| Volume resistivity | IEC 60093 | | Ohm*m | 1E14 |
| Processing conditions for test specimens |
|---|
| 属性名称 | 测试标准 | 测试标准 | 单位 | 数值 |
|---|
| Injection molding - Melt temperature | ISO 294 | | °C | 260 |
| Injection molding - Mold temperature | ISO 294 | | °C | 80 |
| Other properties (23 °C) |
|---|
| 属性名称 | 测试标准 | 测试标准 | 单位 | 数值 |
|---|
| Density | ISO 1183-1 | | kg/m³ | 1220 |
| Glass fiber content | b.o. ISO 3451-1 | Method A | % | 10 |
| Water absorption (equilibrium value) | ISO 62 | 23 °C; 50 % r. h. | % | 0.2 |
| Water absorption (saturation value) | ISO 62 | Water at 23 °C | % | 0.5 |