LEXAN™ 241R resin
PC
SABIC Innovative Plastics
10.5 MFR. Improved flame retardance. Internal mold release.
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 比重 | | | ASTM D792 |
| -- | 1.20 | g/cm³ | ASTM D792 |
| -- | 1.19 | g/cm³ | ASTM D792 |
| 特定体积 | 0.835 | cm³/g | ASTM D792 |
| 熔流率（熔体流动速率） (300°C/1.2 kg) | 11 | g/10 min | ASTM D1238 |
| 收缩率 -
流动 (3.20 mm) | 0.50 到 0.70 | % | 内部方法 |
| 吸水率 | | | ASTM D570 |
| 24 hr | 0.15 | % | ASTM D570 |
| 平衡, 23°C | 0.35 | % | ASTM D570 |
| 平衡, 100°C | 0.58 | % | ASTM D570 |
| 室外适用性 | f2 | | UL 746C |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|
| 洛氏硬度 | | | ASTM D785 |
| M 级 | 70 | | ASTM D785 |
| R 级 | 118 | | ASTM D785 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 抗张强度 1 | | | ASTM D638 |
| 屈服 | 62.1 | MPa | ASTM D638 |
| 断裂 | 68.9 | MPa | ASTM D638 |
| 伸长率 2 | | | ASTM D638 |
| 屈服 | 7.0 | % | ASTM D638 |
| 断裂 | 130 | % | ASTM D638 |
| 弯曲模量 3(50.0 mm 跨距) | 2340 | MPa | ASTM D790 |
| 弯曲强度 4(屈服, 50.0 mm 跨距) | 96.5 | MPa | ASTM D790 |
| 泰伯耐磨性 (1000 Cycles, 1000 g, CS-17 转轮) | 10.0 | mg | ASTM D1044 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 悬壁梁缺口冲击强度 (23°C) | 800 | J/m | ASTM D256 |
| 无缺口悬臂梁冲击 (23°C) | 3200 | J/m | ASTM D4812 |
| 装有测量仪表的落镖冲击 (23°C, Energy at Peak Load) | 63.8 | J | ASTM D3763 |
| 落锤冲击 (23°C) | 169 | J | ASTM D3029 |
| 拉伸冲击强度 5 | 578 | kJ/m² | ASTM D1822 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 载荷下热变形温度 | | | ASTM D648 |
| 0.45 MPa, 未退火, 6.40 mm | 138 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 6.40 mm | 132 | °C | ASTM D648 |
| 维卡软化温度 | 154 | °C | ASTM D1525 6 |
| 线形热膨胀系数 -
流动 (-40 到 95°C) | 6.8E-5 | cm/cm/°C | ASTM E831 |
| 比热 | 1260 | J/kg/°C | ASTM C351 |
| 导热系数 | 0.27 | W/m/K | ASTM C177 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 130 | °C | UL 746 |
| RTI | 130 | °C | UL 746 |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 体积电阻率 | > 1.0E+17 | ohms·cm | ASTM D257 |
| 介电强度 (3.20 mm, in Air) | 15 | kV/mm | ASTM D149 |
| 介电常数 | | | ASTM D150 |
| 50 Hz | 3.17 | | ASTM D150 |
| 60 Hz | 3.17 | | ASTM D150 |
| 1 MHz | 2.96 | | ASTM D150 |
| 耗散因数 | | | ASTM D150 |
| 50 Hz | 9.0E-4 | | ASTM D150 |
| 60 Hz | 9.0E-4 | | ASTM D150 |
| 1 MHz | 0.010 | | ASTM D150 |
| 相比耐漏电起痕指数(CTI) | PLC 2 | | UL 746 |
| 高电弧燃烧指数(HAI) | PLC 1 | | UL 746 |
| 高电压电弧起痕速率 (HVTR) | PLC 2 | | UL 746 |
| 热丝引燃 (HWI) | PLC 2 | | UL 746 |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
|---|
| UL 阻燃等级 | | | UL 94 |
| 1.09 mm | V-2 | | UL 94 |
| 5.99 mm | V-0 | | UL 94 |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 折射率 | 1.586 | | ASTM D542 |
| 透射率 (2540 µm) | 88.0 | % | ASTM D1003 |
| 雾度 (2540 µm) | 1.0 | % | ASTM D1003 |
| 注射 | 额定值 | 单位制 | |
|---|
| 干燥温度 | 121 | °C | |
| 干燥时间 | 3.0 到 4.0 | hr | |
| 干燥时间，最大 | 48 | hr | |
| 建议的最大水分含量 | 0.020 | % | |
| 建议注射量 | 40 到 60 | % | |
| 料筒后部温度 | 271 到 293 | °C | |
| 料筒中部温度 | 282 到 304 | °C | |
| 料筒前部温度 | 293 到 316 | °C | |
| 射嘴温度 | 288 到 310 | °C | |
| 加工（熔体）温度 | 293 到 316 | °C | |
| 模具温度 | 71.1 到 93.3 | °C | |
| 背压 | 0.345 到 0.689 | MPa | |
| 螺杆转速 | 40 到 70 | rpm | |
| 排气孔深度 | 0.025 到 0.076 | mm | |
| 备注 |
|---|
| 1 . | 类型 1, 50 mm/min |
| 2 . | 类型 1, 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Type S |
| 6 . | 标准 B (120°C/h), 载荷2 (50N) |