BCC Resins DP-11-90

PUR，未指定

BCC Products Inc.

产品说明：

DP-11-90 is an unfilled, low viscosity, quick setting two component urethane system. An easy to use 1 to 1 mix ratio (Part A/Part B), DP-11-90 offers the user a 3 minute working time with parts demoldable in as little as 30 minutes. When properly cured, DP-11-90 will exhibit high impact strength and yield thermoplastic-like parts. Some outstanding features include the following:

Mercury free

High impact strength

Moderate heat resistance

No objectionable odor

1 to 1 mix ratio

Excellent finishing properties

Turns tan color upon cure

Thermoplastic appearance

Longer mold life

More parts per day

物性信息：

基本信息
特性	低粘度抗撞击性，高耐热性，中等气味低到无优良外观
外观	棕黄色
形式	液体
加工方法	浇铸

物理性能	额定值	单位制	测试方法
比重	1.10	g/cm³	ASTM D792
特定体积	0.910	cm³/g

热性能	额定值	单位制
Heat Distortion
@ 24 hr room temperature cure	63	°C
@ room temperature cure + 1 hr @ 150°F	79	°C
@ room temperature cure + 1 hr @ 200°F	88	°C

热固性	额定值	单位制	测试方法
Gel Time ¹	3.0	min	ASTM D2471

物理性能	额定值	单位制	测试方法
收缩率 - 流动	0.25	%	ASTM D955

硬度	额定值	单位制	测试方法
肖氏硬度 (邵氏 D)	72 到 78		ASTM D2240

机械性能	额定值	单位制	测试方法
伸长率 (断裂)	11	%	ASTM D638
弯曲模量	2040	MPa	ASTM D790

热固性	额定值	单位制	测试方法
热固组件
部件 A	按重量计算的混合比: 100, 按容量计算的混合比: 100
部件 B	按重量计算的混合比: 100, 按容量计算的混合比: 100
热固性混合粘度			ASTM D2393
-- ²	300	cP	ASTM D2393
-- ³	450	cP	ASTM D2393
-- ⁴	176	cP	ASTM D2393
脱模时间 (25°C)	30 到 60	min

备注
1 .	200 gms
2 .	Mixed
3 .	Part B
4 .	Part A

此数据由承扬从该材料的生产商处获得。承扬尽最大努力确保此数据的准确性，但是承扬对这些数据值不承担任何责任，并强烈建议在最终选料前，就数据值与材料供应商进行验证。