DOWLEX™ 3010

LLDPE

陶氏塑料

产品说明：

DOWLEX™ 3010 Polyethylene Resin is a polyethylene polymer designed to offer high performance properties such as excellent Environmental Stress Crack Resistance (ESCR), tear strength, abrasion resistance, and strong heat seals in thin extrusion coatings.

Linear Low Density Polyethylene

For flexible packaging, overwraps and lamination applications

Complies with:

U.S. FDA 21 CFR 177.1520 (c)

Canadian HPFB No Objection (With Limitations)

EU, No 10/2011

Japan Hygienic Styrene Plastics Association

This resin may be used to manufacture articles for use in packing or holding food during cooking. This statement refers to the extraction limitations only, not to the product's physical utility.

Consult the regulations for complete details.

物性信息：

基本信息
机构评级	FDA 21 CFR 177.1520(c) HPFB (加拿大) No Objection 2 JHOSPA 未评级欧洲 No 10/2011
形式	粒子
加工方法	挤出涂层

物理性能	额定值	单位制	测试方法
比重	0.921	g/cm³	ASTM D792
熔流率（熔体流动速率） (190°C/2.16 kg)	5.4	g/10 min	ASTM D1238

机械性能	额定值	单位制	测试方法
摩擦系数 ¹(与自身 - 动态)	0.60		ASTM D1894

薄膜	额定值	单位制	测试方法
始封温度 ²	115	°C	内部方法
水气透过率 ³	0.63	g·mm/m²/atm/24 hr	ASTM F1249

热性能	额定值	单位制	测试方法
维卡软化温度	100	°C	ASTM D1525
溶融温度（DSC）	124	°C	内部方法

挤出	额定值	单位制	测试方法
熔体温度	316 到 327	°C
内缩量 (321°C, 25.4 µm)	124.5	mm	内部方法
最大生产线速度	8.1	m/sec	内部方法
最小涂层厚度	7.1	µm	内部方法
最小涂层重量	6.8	g/m²	内部方法

挤压说明
挤出涂层薄膜的制造条件：螺杆尺寸：3.5 (89 mm) 30:1 L/D 螺杆类型：带 Maddock Mixer 的单跨型模具间隙：20 密尔 (0.508 mm) 熔体温度：600 °F (315 °C) 输出：250 磅/小时螺杆速度：90 rpm

备注
1 .	1.0 密尔 (25µm) 涂层涂到 50 磅牛皮纸上。
2 .	1.0 密尔 (25µm) 涂层涂到 50 磅牛皮纸上。实现 1 磅/英寸 (4.4 N/25.4 mm) 热封强度的温度。热封强度，Topwave HT 测试仪 0.5 S 保压，40 psi 压力，拉动速度 150 mm/秒。
3 .	1.0 密尔 (25µm) 涂层涂到 50 磅牛皮纸上。