CEFOR™ 1220P
LLDPE
陶氏塑料
CEFOR 1220P is a butene Linear Low Density Polyethylene for general blown film extrusion film applications.
Main Characteristics:
- Used in Industrial, Food & Specialty Packaging
- Better optics and processability
Complies with:
- U.S. FDA 21 177.1520 (c) 3.2a
Consult the regulations for complete details.
Additive:
| 基本信息 | |
|---|
| 添加剂 | - 抗结块剂 (2000 ppm)
- 增滑剂 (1200 ppm)
|
| 机构评级 | - FDA 21 CFR 177.1520(c) 3.2a
- 欧洲 No 10/2011
|
| 形式 | |
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 比重 | 0.919 | g/cm³ | ASTM D792 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| 薄膜 | 额定值 | 单位制 | 测试方法 |
|---|
| 薄膜厚度 - 经测试 | 38 | µm | |
| 膜耐刺穿性 (38 µm) | 5.00 | J/cm³ | 内部方法 |
| 割线模量 | | | ASTM D882 |
| 2% 正割, MD
: 38 µm | 150 | MPa | ASTM D882 |
| 2% 正割, TD
: 38 µm | 145 | MPa | ASTM D882 |
| 抗张强度 | | | ASTM D882 |
| MD
: 屈服, 38 µm | 10.0 | MPa | ASTM D882 |
| TD
: 屈服, 38 µm | 10.0 | MPa | ASTM D882 |
| MD
: 断裂, 38 µm | 33.0 | MPa | ASTM D882 |
| TD
: 断裂, 38 µm | 25.0 | MPa | ASTM D882 |
| 伸长率 | | | ASTM D882 |
| MD
: 断裂, 38 µm | 950 | % | ASTM D882 |
| TD
: 断裂, 38 µm | 1100 | % | ASTM D882 |
| 落锤冲击 (38 µm) | 140 | g | ASTM D1709A |
| 埃尔曼多夫抗撕强度 | | | ASTM D1922 |
| MD
: 38 µm | 220 | g | ASTM D1922 |
| TD
: 38 µm | 330 | g | ASTM D1922 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 维卡软化温度 | 96.7 | °C | ASTM D1525 |
| 溶融温度（DSC） | 116 | °C | 内部方法 |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 光泽度 (45°, 38.1 µm) | 53 | | ASTM D2457 |
| 雾度 (38.1 µm) | 13 | % | ASTM D1003 |
| 挤压说明 |
|---|
| Fabrication Conditions For Blown Film:
Melt Temperature: 428°F (206°C)
Die Gap: 70mil (1.8mm)
Output: 120 lb/hr (54kg/fr)
Blow-Up Ratio: 2.5:1 |
此数据由 承扬 从该材料的生产商处获得。承扬 尽最大努力确保此数据的准确性，但是承扬对这些数据值不承担任何责任，并强烈建议在最终选料前，就数据值与材料供应商进行验证。