| 属性 | 典型值 | UNITS | 测试手段 |
|---|
| MECHANICAL |
|---|
| Tensile Stress, yld, Type I, 50 mm/min | 57 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 50 mm/min | 47 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 50 mm/min | 5 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 100 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 2270 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 88 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2300 | MPa | ASTM D790 |
| Taber Abrasion, CS-17, 1 kg | 63 | mg/1000cy | SABIC method |
| Tensile Stress, yield, 5 mm/min | 55 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 45 | MPa | ISO 527 |
| Tensile Stress, yield, 50 mm/min | 55 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 45 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 5 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 100 | % | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 4 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | >50 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2400 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 80 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2300 | MPa | ISO 178 |
| Ball Indentation Hardness, H358/30 | 96 | MPa | ISO 2039-1 |
| Hardness, Rockwell R | 115 | - | ISO 2039-2 |
| IMPACT |
|---|
| Izod Impact, notched, 23°C | 580 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 480 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy, 23°C | 54 | J | ASTM D3763 |
| Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 40 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 20 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 45 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 18 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| THERMAL |
|---|
| Vicat Softening Temp, Rate B/50 | 130 | °C | ASTM D1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 112 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 7.2E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 7.2E-05 | 1/°C | ASTM E831 |
| Thermal Conductivity | 0.2 | W/m-°C | ISO 8302 |
| CTE, 23°C to 60°C, flow | 8.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/50 | 126 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 128 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 122 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 102 | °C | ISO 75/Ae |
| Relative Temp Index, Elec | 105 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 80 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 105 | °C | UL 746B |
| PHYSICAL |
|---|
| Specific Gravity | 1.15 | - | ASTM D792 |
| Mold Shrinkage on Tensile Bar, flow | 0.5-0.7 | % | SABIC method |
| Mold Shrinkage, flow, 3.2 mm | 0.5-0.7 | % | SABIC method |
| Melt Flow Rate, 260°C/5.0 kgf | 24 | g/10 min | ASTM D1238 |
| Density | 1.15 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/saturated) | 0.6 | % | ISO 62-1 |
| Moisture Absorption (23°C / 50% RH) | 0.2 | % | ISO 62 |
| Melt Volume Rate, MVR at 260°C/2.16 kg | 8 | cm³/10 min | ISO 1133 |
| Melt Volume Rate, MVR at 260°C/5.0 kg | 22 | cm³/10 min | ISO 1133 |
| ELECTRICAL |
|---|
| Volume Resistivity | >1.E+15 | Ω.cm | IEC 60093 |
| Surface Resistivity, ROA | >1.E+15 | Ω | IEC 60093 |
| Dielectric Strength, in oil, 0.8 mm | 35 | kV/mm | IEC 60243-1 |
| Dielectric Strength, in oil, 1.6 mm | 25 | kV/mm | IEC 60243-1 |
| Dielectric Strength, in oil, 3.2 mm | 17 | kV/mm | IEC 60243-1 |
| Relative Permittivity, 1 MHz | 2.7 | - | IEC 60250 |
| Dissipation Factor, 50/60 Hz | 0.002 | - | IEC 60250 |
| Dissipation Factor, 1 MHz | 0.007 | - | IEC 60250 |
| Comparative Tracking Index | 250 | V | IEC 60112 |
| Relative Permittivity, 50/60 Hz | 2.8 | - | IEC 60250 |
| FLAME CHARACTERISTICS |
|---|
| UL Yellow Card Link | E45329-236710 | - | - |
| UL Recognized, 94HB Flame Class Rating | 1.2 | mm | UL 94 |
| UL Recognized, 94HB Flame Class Rating 2nd value | 3 | mm | UL 94 |
| Glow Wire Flammability Index 650°C, passes at | 1 | mm | IEC 60695-2-12 |
| Oxygen Index (LOI) | 23 | % | ISO 4589 |
| Injection Molding |
|---|
| Drying Temperature | 100-110 | °C | |
| Drying Time | 2-4 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 260-290 | °C | |
| Nozzle Temperature | 240-280 | °C | |
| Front - Zone 3 Temperature | 250-290 | °C | |
| Middle - Zone 2 Temperature | 250-290 | °C | |
| Rear - Zone 1 Temperature | 230-260 | °C | |
| Hopper Temperature | 60-80 | °C | |
| Mold Temperature | 60-90 | °C | |