| 属性 | 典型值 | UNITS | 测试手段 |
|---|
| MECHANICAL |
|---|
| Tensile Stress, yld, Type I, 5 mm/min | 39 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 30 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 5 mm/min | 3.1 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 32 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 2080 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 66 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2160 | MPa | ASTM D790 |
| Hardness, Rockwell R | 102 | - | ASTM D785 |
| Tensile Stress, yield, 50 mm/min | 41 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 30 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 2.6 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 21 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 1970 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 60 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2000 | MPa | ISO 178 |
| IMPACT |
|---|
| Izod Impact, notched, 23°C | 432 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 299 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy, 23°C | 37 | J | ASTM D3763 |
| Izod Impact, notched 80*10*4 +23°C | 35 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 23 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 37 | kJ/m² | ISO 179/1eA |
| THERMAL |
|---|
| Vicat Softening Temp, Rate B/50 | 106 | °C | ASTM D1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 91 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 76 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 1.01E-04 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 1.04E-04 | 1/°C | ASTM E831 |
| Vicat Softening Temp, Rate B/50 | 95 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 97 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 78 | °C | ISO 75/Af |
| Relative Temp Index, Elec | 60 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 60 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 60 | °C | UL 746B |
| PHYSICAL |
|---|
| Specific Gravity | 1.03 | - | ASTM D792 |
| Mold Shrinkage, flow, 3.2 mm | 0.6-0.8 | % | SABIC method |
| Melt Viscosity, 240°C, 100 sec-1 | 15500 | Poise | ASTM D3825 |
| Density | 1.03 | g/cm³ | ISO 1183 |
| Melt Flow Rate, 220°C/10.0 kg | 4 | g/10 min | ISO 1133 |
| ELECTRICAL |
|---|
| Arc Resistance, Tungsten {PLC} | 5 | PLC Code | ASTM D495 |
| Hot Wire Ignition {PLC) | 4 | PLC Code | UL 746A |
| High Voltage Arc Track Rate {PLC} | 1 | PLC Code | UL 746A |
| High Ampere Arc Ign, surface {PLC} | 4 | PLC Code | UL 746A |
| Comparative Tracking Index (UL) {PLC} | 0 | PLC Code | UL 746A |
| FLAME CHARACTERISTICS |
|---|
| UL Yellow Card Link | E45329-103353495 | - | - |
| UL Recognized, 94HB Flame Class Rating | 1.5 | mm | UL 94 |
| Sheet Extrusion |
|---|
| Drying Temperature | 80-95 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 215-260 | °C | |
| Barrel - Zone 1 Temperature | 170-200 | °C | |
| Barrel - Zone 2 Temperature | 180-220 | °C | |
| Barrel - Zone 3 Temperature | 190-225 | °C | |
| Barrel - Zone 4 Temperature | 200-240 | °C | |
| Adapter Temperature | 205-250 | °C | |
| Die Temperature | 205-250 | °C | |
| Roll Stack Temp - Top | 90-95 | °C | |
| Roll Stack Temp - Middle | 95-105 | °C | |
| Roll Stack Temp - Bottom | 100-105 | °C | |