ULTEM™ 1000RV resin
PEI
SABIC Innovative Plastics
Standard flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing; color dependant, see UL Yellow Card.
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 比重 | | | |
| -- | 1.27 | g/cm³ | ASTM D792 |
| -- | 1.25 | g/cm³ | ISO 1183 |
| 熔流率（熔体流动速率） (337°C/6.6 kg) | 9.7 | g/10 min | ASTM D1238 |
| 溶化体积流率（MVR） (220°C/5.0 kg) | 13.0 | cm³/10min | ISO 1133 |
| 收缩率 -
流动 (3.20 mm) | 0.50 到 0.70 | % | 内部方法 |
| 吸水率 | | | ISO 62 |
| 饱和, 23°C | 1.3 | % | ISO 62 |
| 平衡, 23°C, 50% RH | 0.70 | % | ISO 62 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 拉伸模量 | | | |
| -- 1 | 3590 | MPa | ASTM D638 |
| -- | 3200 | MPa | ISO 527-2/1 |
| 抗张强度 | | | |
| 屈服 2 | 110 | MPa | ASTM D638 |
| 屈服 | 105 | MPa | ISO 527-2/5 |
| 断裂 3 | 90.0 | MPa | ASTM D638 |
| 断裂 | 85.0 | MPa | ISO 527-2/5 |
| 伸长率 | | | |
| 屈服 4 | 7.0 | % | ASTM D638 |
| 屈服 | 6.0 | % | ISO 527-2/5 |
| 断裂 5 | 60 | % | ASTM D638 |
| 断裂 | 60 | % | ISO 527-2/5 |
| 弯曲模量 | | | |
| 50.0 mm 跨距 6 | 3440 | MPa | ASTM D790 |
| -- 7 | 3300 | MPa | ISO 178 |
| 弯曲应力 | | | |
| -- | 160 | MPa | ISO 178 |
| 屈服, 50.0 mm 跨距 8 | 173 | MPa | ASTM D790 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 简支梁缺口冲击强度 9(23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| 悬壁梁缺口冲击强度 | | | |
| -30°C | 55 | J/m | ASTM D256 |
| 23°C | 53 | J/m | ASTM D256 |
| -30°C 10 | 6.0 | kJ/m² | ISO 180/1A |
| 23°C 11 | 6.0 | kJ/m² | ISO 180/1A |
| 无缺口悬臂梁冲击 (23°C) | 1300 | J/m | ASTM D4812 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 载荷下热变形温度 | | | |
| 1.8 MPa, 未退火, 6.40 mm | 201 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 64.0 mm 跨距 12 | 215 | °C | ISO 75-2/Af |
| 维卡软化温度 | | | |
| -- | 219 | °C | ASTM D1525 13 |
| -- | 215 | °C | ISO 306/B50 |
| -- | 211 | °C | ISO 306/B120 |
| 线形热膨胀系数 | | | |
| 流动
: -20 到 150°C | 5.6E-5 | cm/cm/°C | ASTM E831 |
| 流动
: -40 到 40°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| 横向
: -20 到 150°C | 5.4E-5 | cm/cm/°C | ASTM E831 |
| 横向
: -40 到 40°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 170 | °C | UL 746 |
| RTI Imp | 170 | °C | UL 746 |
| RTI | 170 | °C | UL 746 |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 体积电阻率 | 1.0E+17 | ohms·cm | ASTM D257 |
| 介电强度 | | | ASTM D149 |
| 1.60 mm, in Air | 33 | kV/mm | ASTM D149 |
| 1.60 mm, in Oil | 28 | kV/mm | ASTM D149 |
| 介电常数 (1 kHz) | 3.15 | | ASTM D150 |
| 耗散因数 | | | ASTM D150 |
| 1 kHz | 1.3E-3 | | ASTM D150 |
| 2.45 GHz | 2.5E-3 | | ASTM D150 |
| 耐电弧性 14 | PLC 5 | | ASTM D495 |
| 相比耐漏电起痕指数(CTI) | PLC 4 | | UL 746 |
| 高电弧燃烧指数(HAI) | PLC 3 | | UL 746 |
| 高电压电弧起痕速率 (HVTR) | PLC 2 | | UL 746 |
| 热丝引燃 (HWI) | PLC 1 | | UL 746 |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
|---|
| UL 阻燃等级 | | | UL 94 |
| 0.400 mm | V-2 | | UL 94 |
| 0.750 mm | V-1
V-0 | | UL 94 |
| 3.00 mm | 5VA | | UL 94 |
| 极限氧指数 | 47 | % | ASTM D2863 |
| NBS Smoke Density -
Flaming, Ds, 4 min | 0.700 | | ASTM E662 |
| 注射 | 额定值 | 单位制 | |
|---|
| 干燥温度 | 149 | °C | |
| 干燥时间 | 4.0 到 6.0 | hr | |
| 干燥时间，最大 | 24 | hr | |
| 建议的最大水分含量 | 0.020 | % | |
| 建议注射量 | 40 到 60 | % | |
| 料筒后部温度 | 332 到 399 | °C | |
| 料筒中部温度 | 338 到 399 | °C | |
| 料筒前部温度 | 343 到 399 | °C | |
| 射嘴温度 | 343 到 399 | °C | |
| 加工（熔体）温度 | 349 到 399 | °C | |
| 模具温度 | 135 到 163 | °C | |
| 背压 | 0.345 到 0.689 | MPa | |
| 螺杆转速 | 40 到 70 | rpm | |
| 排气孔深度 | 0.025 到 0.076 | mm | |
| 备注 |
|---|
| 1 . | 5.0 mm/min |
| 2 . | 类型 1, 5.0 mm/min |
| 3 . | 类型 1, 5.0 mm/min |
| 4 . | 类型 1, 5.0 mm/min |
| 5 . | 类型 1, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 标准 B (120°C/h), 载荷2 (50N) |
| 14 . | 钨电极 |
此数据由 承扬 从该材料的生产商处获得。承扬 尽最大努力确保此数据的准确性，但是承扬对这些数据值不承担任何责任，并强烈建议在最终选料前，就数据值与材料供应商进行验证。