LEXAN™ EXL1414 resin
PC
SABIC Innovative Plastics
产品说明：
LEXAN EXL1414 polycarbonate (PC) siloxane copolymer resin is a medium flow opaque injection molding (IM) grade. This resin offers extreme low temperature (-40 C) ductility in combination with excellent processability and release with opportunities for shorter IM cycle times compared to standard PC. LEXAN EXL1414 resin is a product available in wide range of opaque colors and may be an excellent candidate for a wide variety of applications.
物性信息：
基本信息 特性 共聚物 可加工性，良好 快的成型周期 流动性中等 通用 脱模性能良好 延展性 用途 外观 加工方法 多点数据 Coefficient of Thermal Expansion vs. Temperature (ASTM E831) Flexural DMA (ASTM D4065) Pressure-Volume-Temperature (PVT - Zoller Method) Shear DMA (ASTM D4065) Specific Heat vs. Temperature (ASTM D3417) Tensile Fatigue Tensile Stress vs. Strain (ASTM D638) Thermal Conductivity vs. Temperature (ASTM E1530) Viscosity vs. Shear Rate (ASTM D3835)
物理性能 额定值 单位制 测试方法 比重 -- 1.18 g/cm³ ASTM D792 -- 1.19 g/cm³ ISO 1183 熔流率（熔体流动速率） (300°C/1.2 kg) 10 g/10 min ASTM D1238 溶化体积流率（MVR） (300°C/1.2 kg) 9.00 cm³/10min ISO 1133 收缩率 内部方法 流动
: 3.20 mm 0.40 到 0.80 % 内部方法 横向流动
: 3.20 mm 0.40 到 0.80 % 内部方法 吸水率 ISO 62 饱和, 23°C 0.35 % ISO 62 平衡, 23°C, 50% RH 0.15 % ISO 62
硬度 额定值 单位制 测试方法 洛氏硬度 ASTM D785 L 计秤 89 ASTM D785 R 级 121 ASTM D785
机械性能 额定值 单位制 测试方法 拉伸模量 -- 1 2020 MPa ASTM D638 -- 2150 MPa ISO 527-2/1 抗张强度 屈服 2 55.5 MPa ASTM D638 屈服 57.0 MPa ISO 527-2/50 断裂 3 50.3 MPa ASTM D638 断裂 60.0 MPa ISO 527-2/50 伸长率 屈服 4 6.0 % ASTM D638 屈服 6.0 % ISO 527-2/50 断裂 5 98 % ASTM D638 断裂 120 % ISO 527-2/50 弯曲模量 50.0 mm 跨距 6 2230 MPa ASTM D790 -- 7 2250 MPa ISO 178 弯曲应力 -- 85.0 MPa ISO 178 屈服, 50.0 mm 跨距 8 92.4 MPa ASTM D790
冲击性能 额定值 单位制 测试方法 简支梁缺口冲击强度 9 ISO 179/1eA -30°C 65 kJ/m² ISO 179/1eA 23°C 70 kJ/m² ISO 179/1eA 简支梁无缺口冲击强度 10 ISO 179/1eU -30°C 无断裂 ISO 179/1eU 23°C 无断裂 ISO 179/1eU 悬壁梁缺口冲击强度 -30°C 770 J/m ASTM D256 23°C 870 J/m ASTM D256 -30°C 11 60 kJ/m² ISO 180/1A 23°C 12 70 kJ/m² ISO 180/1A 无缺口伊佐德冲击强度 13 ISO 180/1U -30°C 无断裂 ISO 180/1U 23°C 无断裂 ISO 180/1U 装有测量仪表的落镖冲击 (23°C, Total Energy) 70.0 J ASTM D3763
热性能 额定值 单位制 测试方法 载荷下热变形温度 0.45 MPa, 未退火, 3.20 mm 139 °C ASTM D648 0.45 MPa, 未退火, 100 mm 跨距 14 140 °C ISO 75-2/Be 1.8 MPa, 未退火, 3.20 mm 124 °C ASTM D648 1.8 MPa, 未退火, 100 mm 跨距 15 128 °C ISO 75-2/Ae 维卡软化温度 -- 145 °C ASTM D1525, ISO 306/B50 11 16 -- 146 °C ISO 306/B120 Ball Pressure Test (125°C) Pass IEC 60695-10-2 线形热膨胀系数 流动
: -40 到 40°C 7.0E-5 cm/cm/°C ASTM E831 流动
: 23 到 80°C 7.2E-5 cm/cm/°C ISO 11359-2 横向
: -40 到 40°C 7.5E-5 cm/cm/°C ASTM E831 横向
: 23 到 80°C 7.2E-5 cm/cm/°C ISO 11359-2 RTI Elec 130 °C UL 746 RTI Imp 120 °C UL 746 RTI 125 °C UL 746
电气性能 额定值 单位制 测试方法 表面电阻率 > 1.0E+15 ohms ASTM D257 体积电阻率 > 1.0E+15 ohms·cm ASTM D257 介电强度 (0.800 mm, in Oil) 16 kV/mm ASTM D149 介电常数 ASTM D150 100 Hz 2.68 ASTM D150 1 MHz 2.64 ASTM D150 耗散因数 ASTM D150 100 Hz 1.2E-3 ASTM D150 1 MHz 9.3E-3 ASTM D150
可燃性 额定值 单位制 测试方法 UL 阻燃等级 (0.400 mm) HB UL 94 灼热丝易燃指数 IEC 60695-2-12 0.800 mm 850 °C IEC 60695-2-12 1.00 mm 960 °C IEC 60695-2-12 热灯丝点火温度 IEC 60695-2-13 1.00 mm 875 °C IEC 60695-2-13 3.00 mm 875 °C IEC 60695-2-13
注射 额定值 单位制 干燥温度 121 °C 干燥时间 3.0 到 4.0 hr 干燥时间，最大 48 hr 建议的最大水分含量 0.020 % 建议注射量 40 到 60 % 料筒后部温度 217 到 293 °C 料筒中部温度 282 到 304 °C 料筒前部温度 293 到 316 °C 射嘴温度 288 到 310 °C 加工（熔体）温度 293 到 316 °C 模具温度 71.0 到 93.0 °C 背压 0.345 到 0.689 MPa 螺杆转速 40 到 70 rpm 排气孔深度 0.025 到 0.076 mm
备注 1 . 50 mm/min 2 . 类型 1, 50 mm/min 3 . 类型 1, 50 mm/min 4 . 类型 1, 50 mm/min 5 . 类型 1, 50 mm/min 6 . 1.3 mm/min 7 . 2.0 mm/min 8 . 1.3 mm/min 9 . 80*10*3 sp=62mm 10 . 80*10*3 sp=62mm 11 . 80*10*3 12 . 80*10*3 13 . 80*10*3 14 . 120*10*4 mm 15 . 120*10*4 mm 16 . 标准 B (120°C/h), 载荷2 (50N)
此数据由 承扬 从该材料的生产商处获得。承扬 尽最大努力确保此数据的准确性，但是承扬对这些数据值不承担任何责任，并强烈建议在最终选料前，就数据值与材料供应商进行验证。